XW-10 
 A hardened in the air or oil, chromium, molybdenum, vanadium alloy tool steel, its characteristics are: 
 ? Machining performance 
 ? Have high dimensional stability after hardening 
 ? High compressive strength 
 ? Good hardenability 
 ? Good wear resistance 

 Chemical Composition% C 
 1.0 of Si 
 0.3 of Mn 
 0.6 of Cr 
 5.3 of Mo 
 1.1 V 
 0.2 
 Standard specification AISIA2, BA2 W.-Nr.1.2363, 
 Delivery status of soft annealed to a hardness of about 215HB 
 Color-coded red / green 

 Use 
 ________________________________________ 
 In the the ASSAB tool steel, the XW-10 performance in the DF-3 and XW-42, because it combines good wear resistance and toughness, it is often referred to as "universal" cold steel. 
 XW-10 with good toughness make cutting tools in machining, have a good chipping resistance. 
 In practical applications, the XW-10 molds is more profitable than comparable high-chromium steel mold. 

 ________________________________________ Punching processing 
 ________________________________________ 
 Material thickness 
 (Mm) Hardness 
 HRC 
 Molds for: 
 Blanking, punching empty 
 Perforation, cutting head, 
 Shearing, trimming, 
 Shear 
 Maximum three 
 3-6 
 6-10 
 60-62 
 56-60 
 54-56 
 Cold cut 
 Processing of waste plastics rotary shear blades 
 Forgings cut, trimming mold high temperature 
 At room temperature 
 56-60 
 58-60 
 56-58 

 ________________________________________ Molding 
 ________________________________________ 
 Hardness 
 HRC 
 Molds for: 
 Bending, stretching, curling, spinning, molding and rotary extrusion 
 Pressure die 
 Tubes and profiles forming the tie rod 
 Cold complex mode with a female mold 
 Type anvil 
 Gauge, measuring; rail 
 Sleeve, the sleeve, knurled mode. 
 Wear plastic molding and core 
 56-62 
 56-60 
 58-62 
 58-60 
 56-60 
 58-62 
 58-62 


 ________________________________________ 
 Microstructure 
 ________________________________________ 
 XW-10 compare with similar high-carbon high chrome steel carbide particles. 



 Physical properties 
 ________________________________________ 
 XW-10 hardened and tempered to 62HRC, when the room temperature and slightly higher temperature physical properties. 
 Temperature of 20 ° C to 200 ° C to 400 ℃ 
 Density 
 Kg/m3 7750 7700 7650 
 Coefficient of elasticity 
 In N/mm2 190 000 185 000 170 000 
 Thermal expansion coefficient of 20 ° C / ° C - 11.6x10-6 11.3x10-6 
 Thermal conductivity W / m ℃ 26.0 27.0 28.5 
 Specific heat 
 J / kg ℃ 460 - 

 Compressive strength 
 ________________________________________ 
 Approximation: 
 Hardness 
 The HRC compression yield strength Rc0.2 of 
 Rm Rp0.2 
 N/MM2 N / si 
 622,200,319 
 602,150,312 
 551,800,261 
 501,350,196 





 The above mold XW-10 manufacturing, the grinding time to produce three million products. 